Question 1

Product Description

Accepted Answer

3M™ High Performance Acrylic Adhesive 200MP is often used for graphic attachment and general industrial bonding applications. It offers excellent adhesion to metal and high surface energy plastics. This adhesive offers some initial repositionability for accurate placement when bonding to plastics. The adhesive has good resistance to moisture and hot/cold cycles.

Question 2

Construction

Accepted Answer

Short-term temperature resistance up to 205 °C.
Good resistance to solvents and moisture.
High shear strength against slippage and edge lift.
Available in thicknesses of 0.06 and 0.13 mm with single or double liner.
The adhesive color is transparent with a very slight yellowish tint, which is usually not visible in a single adhesive layer.
Special polycoated &#8220;Kraft Layflat Liner&#8221; for increased dimensional stability during storage, processing, shipping and application under high humidity.

Question 3

Performance characteristics

Accepted Answer

Long-term bonding of graphic nameplates and overlays (reverse-printed polycarbonate or polyester) to metal and plastics with high surface energy.
Bonding of metal signs and nameplates.
Bonding of graphic and backlit overlays.
High-speed processing of parts (medical components, permanent labels, flexible circuits).
Lamination onto industrial foams for rotary die-cutting of gaskets.

Typical performance characteristics
90° Peel adhesion according to ASTM D3330
(300 mm/min, covered with aluminum tape)

Substrate
Cleaning
Dwell time
Test temperature
467MP · 467MPF · 467MC · 9667MP · 7952MP · 7962MP
468MP · 468MPF · 468MC · 9668MP · 7955MP · 7965MP

Stainless steel
MEK and Acetone
15 minutes
23 °C
8.3 N/cm
12.6 N/cm

Stainless steel
MEK and Acetone
72 hours
23 °C
12.7 N/cm
18.2 N/cm

Stainless steel
MEK and Acetone
72 hours
70 °C
11.6 N/cm
18.6 N/cm

Aluminum
IPA
72 hours
23 °C
10.7 N/cm
17.5 N/cm

PET
IPA
72 hours
23 °C
9.4 N/cm
10.0 N/cm

PC
IPA
72 hours
23 °C
9.8 N/cm
12.3 N/cm

PMMA
IPA / Water 1:1
72 hours
23 °C
9.4 N/cm
13.3 N/cm

Glass
IPA
72 hours
23 °C
13.3 N/cm
22.2 N/cm

ABS
IPA
72 hours
23 °C
8.1 N/cm
11.4 N/cm

PVC
IPA
72 hours
23 °C
8.6 N/cm
12.5 N/cm

MEK: Methyl-Ethyl-Ketone; IPA: Isopropanol
 
180° Peel adhesion according to ASTM D3330
(300 mm/min, covered with PET)

Substrate
Cleaning
Dwell time
Test temperature
467MP · 467MPF · 467MC · 9667MP · 7952MP · 7962MP
468MP · 468MPF · 468MC · 9668MP · 7955MP · 7965MP

Stainless steel
MEK and Aceton
72 hours
23 °C
7.2 N/cm
10.4 N/cm

MEK: Methyl-Ethyl-Ketone
 
Dynamic shear strength according to ASTM D1002

Substrate
Cleaning
Dwell time
Test temperature
467MP · 467MPF · 467MC · 9667MP · 7952MP · 7962MP
468MP · 468MPF · 468MC · 9668MP · 7955MP · 7965MP

Aluminum
12.7 × 25.4 mm
n-Heptane and IPA
72 hours
23 °C
0.5 MPa
0.9 MPa

IPA: Isopropanol
 
Static shear strength according to FINAT FTM8

Substrate
Cleaning
Weight
Test temperature
467MP · 467MPF · 467MC · 9667MP · 7952MP · 7962MP
468MP · 468MPF · 468MC · 9668MP · 7955MP · 7965MP

Aluminum
12.7 × 25.4 mm
n-Heptane and IPA
1000 g
23 °C
>10000 minutes
>10000 minutes

IPA: Isopropanol
 
Shear Adhesion Failure Temperature (S.A.F.T) according to AFERA 5013

Substrate
Cleaning
Temperature profile
Weight
467MP · 467MPF · 467MC · 9667MP · 7952MP · 7962MP
468MP · 468MPF · 468MC · 9668MP · 7955MP · 7965MP

Aluminum
12.7 × 25.4 mm
n-Heptane and IPA
40 °C to 205 °C,
0.5 °C/min
500 g
>205 °C
>205 °C

Aluminum
12.7 × 25.4 mm
n-Heptane and IPA
40 °C to 205 °C,
0.5 °C/min
1000 g
>160 °C
>160 °C

IPA: Isopropanol
 
90° Peel adhesion according to ASTM D3330 after condensation
(300 mm/min)

Substrate
Cleaning
Temperature / Humidity
Duration
467MP · 467MPF · 467MC · 9667MP · 7952MP · 7962MP
468MP · 468MPF · 468MC · 9668MP · 7955MP · 7965MP

Aluminum
n-Heptane and IPA
38 °C / 98 %
7 days
12.3 N/cm
26.5 N/cm

IPA: Isopropanol
 
90° Peel adhesion according to ASTM D3330 after temperature aging test
(300 mm/min)

Substrate
Cleaning
Temperature / Humidity
(3 cycles = 72 hours)
Reconditioning @ RT
467MP · 467MPF · 467MC · 9667MP · 7952MP · 7962MP
468MP · 468MPF · 468MC · 9668MP · 7955MP · 7965MP

Aluminum
n-Heptane and IPA
4h @ -40°C, 4h @ +90°C,
16h @ 38°C / 98% rh
24 hours
10.6 N/cm
24 N/cm

IPA: Isopropanol
 
UV resistance according to DIN EN ISO 4892-3

Substrate
Cleaning
Duration
467MP · 467MPF · 467MC · 9667MP · 7952MP · 7962MP
468MP · 468MPF · 468MC · 9668MP · 7955MP · 7965MP

Aluminum
n-Heptane and IPA
1000 hours
No visual changes

IPA: Isopropanol
 
90° Peel adhesion according to ASTM D3330 after chemical storage
(300 mm/min)

Chemical
Substrate
Duration
Reconditioning
467MP · 467MPF · 467MC · 9667MP · 7952MP · 7962MP
468MP · 468MPF · 468MC · 9668MP · 7955MP · 7965MP

Gasoline Super E5
Aluminum
1 hour
24 hours @23 °C
9.3 N/cm
20.2 N/cm

MEK
Aluminum
1 hour
24 hours @23 °C
7.8 N/cm
17.3 N/cm

Sulfuric acid 5%
Aluminum
1 hour
24 hours @23 °C
11.0 N/cm
22.3 N/cm

Engine oil 5W30
Aluminum
1 hour
24 hours @23 °C
11.0 N/cm
22.0 N/cm

Distilled water
Aluminum
100 hours
24 hours @23 °C
10.2 N/cm
21.9 N/cm

Salt water 5%
Aluminum
72 hours
24 hours @23 °C
11.9 N/cm
23.2 N/cm

Caustic solution pH10
Stainless steel
1 hour
24 hours @23 °C
11.3 N/cm
18.1 N/cm

Electrical properties

Electrical property
467MP · 467MPF · 467MC · 9667MP · 7952MP · 7962MP
468MP · 468MPF · 468MC · 9668MP · 7955MP · 7965MP

Breakdown voltage (DIN EN 60243-1 / VDE 0303-21)
1800 V
5000 V

Insulation resistance (DIN EN 62631-3-1 / VDE 0307-3-1)
>4 × 10^13 Ω
>1.5 × 10^13 Ω

Dielectric strength (DIN EN 60243-1 / VDE 0303-21)
32 kV/mm
37 kV/mm

Question 4

Processing

Accepted Answer

Product
Total thickness¹ (without liner)
Liner²

Type
Thickness
Color
Print
Note

467MP
0.06 mm
58# Polycoated Kraft
0.11 mm
tan
3M 467MP 200MP Adhesive

467MPF
Polyester (PET)
0.05 mm
clear
no print

467MC
58# Polycoated Kraft Micro Chanel Liner
0.11 mm
tan
no print

9667MP
0.06 mm
83# Polycoated Kraft
0.16 mm
tan
3M 200MP

7952MP
0.06 mm
1) 58# Polycoated Kraft
2) 58# Polycoated Kraft
1) 0.11 mm
2) 0.11 mm
tan
3M 200MP
Double lined, available in both roll and sheet form

7962MP
1) 58# Polycoated Kraft
2) 58# Polycoated Kraft
1) 0.16 mm
2) 0.11 mm
tan
3M 200MP

468MP
0.13 mm
58# Polycoated Kraft
0.11 mm
tan
3M 468MP 200MP Adhesive

468MPF
Polyester (PET)
0.05 mm
clear
no print

468MC
58# Polycoated Kraft Micro Chanel Liner
0.11 mm
tan
no print

9668MP
0.13 mm
83# Polycoated Kraft
0.16 mm
tan
3M 200MP

7955MP
0.13 mm
1) 58# Polycoated Kraft
2) 58# Polycoated Kraft
1) 0.11 mm
2) 0.11 mm
tan
3M 200MP
Double lined, available in both roll and sheet form

7965MP
1) 83# Polycoated Kraft
2) 58# Polycoated Kraft
1) 0.16 mm
2) 0.11 mm
tan
3M 200MP

¹The thickness indicated is based on a calculation from manufacturing-controlled adhesive coat weights using a density of 1.012 g/cm3
²Where two liners are listed (two-line products, useful for selective die-cutting), liner 1) is the primary (remains with the die-cut part); liner 2)

Question 5

Storage

Accepted Answer

Store at 15 °C-25 °C and 40-60% relative humidity in the original packaging. The product can be stored for up to 18 months after the date of manufacture.

Question 6

Durability

Accepted Answer

The shelf life may be shortened if the original packaging is not properly sealed or is stored in an environment with high temperatures or high humidity. The shelf life is intended for the storage of the non-converted 3M product. Please click or scan the QR code to read the technical bulletin “Shelf-Life Statements on Select Converter Markets Products” for more information.

Question 7

Further information

Accepted Answer

Further test reports and certifications
3M can offer extended data for various test conditions and substrates as well as certifications. Please contact your 3M sales representative or application engineer. Please contact your local 3M office. You can click or scan the QR code to see the contact details, or visit www.3M.com.   
 
3M™ Material Data Card (MDC) for Finite Element Analysis (FEA)
FEA modeling is a tool that helps designers choose the right adhesive system for the application requirements. 3M can offer elastic-plastic modeling data at various strain rates for most of our adhesives. We also know and support other modeling conditions and methods. Please click or scan the QR code to request the 3M Material Data Card for your modeling.   
 
3M™ Bonding Process Center
3M™ Bonding Process Centers around the world can address application issues. Please click or scan the QR code to arrange a personal or virtual visit to try out new innovations in dispensing and automation and to find customized solutions for production problems.

Substrate	Cleaning	Dwell time	Test temperature	467MP · 467MPF · 467MC · 9667MP · 7952MP · 7962MP	468MP · 468MPF · 468MC · 9668MP · 7955MP · 7965MP
Stainless steel	MEK and Acetone	15 minutes	23 °C	8.3 N/cm	12.6 N/cm
Stainless steel	MEK and Acetone	72 hours	23 °C	12.7 N/cm	18.2 N/cm
Stainless steel	MEK and Acetone	72 hours	70 °C	11.6 N/cm	18.6 N/cm
Aluminum	IPA	72 hours	23 °C	10.7 N/cm	17.5 N/cm
PET	IPA	72 hours	23 °C	9.4 N/cm	10.0 N/cm
PC	IPA	72 hours	23 °C	9.8 N/cm	12.3 N/cm
PMMA	IPA / Water 1:1	72 hours	23 °C	9.4 N/cm	13.3 N/cm
Glass	IPA	72 hours	23 °C	13.3 N/cm	22.2 N/cm
ABS	IPA	72 hours	23 °C	8.1 N/cm	11.4 N/cm
PVC	IPA	72 hours	23 °C	8.6 N/cm	12.5 N/cm

Substrate	Cleaning	Temperature profile	Weight	467MP · 467MPF · 467MC · 9667MP · 7952MP · 7962MP	468MP · 468MPF · 468MC · 9668MP · 7955MP · 7965MP
Aluminum 12.7 × 25.4 mm	n-Heptane and IPA	40 °C to 205 °C, 0.5 °C/min	500 g	>205 °C	>205 °C
Aluminum 12.7 × 25.4 mm	n-Heptane and IPA	40 °C to 205 °C, 0.5 °C/min	1000 g	>160 °C	>160 °C

Chemical	Substrate	Duration	Reconditioning	467MP · 467MPF · 467MC · 9667MP · 7952MP · 7962MP	468MP · 468MPF · 468MC · 9668MP · 7955MP · 7965MP
Gasoline Super E5	Aluminum	1 hour	24 hours @23 °C	9.3 N/cm	20.2 N/cm
MEK	Aluminum	1 hour	24 hours @23 °C	7.8 N/cm	17.3 N/cm
Sulfuric acid 5%	Aluminum	1 hour	24 hours @23 °C	11.0 N/cm	22.3 N/cm
Engine oil 5W30	Aluminum	1 hour	24 hours @23 °C	11.0 N/cm	22.0 N/cm
Distilled water	Aluminum	100 hours	24 hours @23 °C	10.2 N/cm	21.9 N/cm
Salt water 5%	Aluminum	72 hours	24 hours @23 °C	11.9 N/cm	23.2 N/cm
Caustic solution pH10	Stainless steel	1 hour	24 hours @23 °C	11.3 N/cm	18.1 N/cm

Electrical property	467MP · 467MPF · 467MC · 9667MP · 7952MP · 7962MP	468MP · 468MPF · 468MC · 9668MP · 7955MP · 7965MP
Breakdown voltage (DIN EN 60243-1 / VDE 0303-21)	1800 V	5000 V
Insulation resistance (DIN EN 62631-3-1 / VDE 0307-3-1)	>4 × 10^13 Ω	>1.5 × 10^13 Ω
Dielectric strength (DIN EN 60243-1 / VDE 0303-21)	32 kV/mm	37 kV/mm

Product	Total thickness¹ (without liner)	Liner²
Product	Total thickness¹ (without liner)	Type	Thickness	Color	Print	Note
467MP	0.06 mm	58# Polycoated Kraft	0.11 mm	tan	3M 467MP 200MP Adhesive
467MPF		Polyester (PET)	0.05 mm	clear	no print
467MC		58# Polycoated Kraft Micro Chanel Liner	0.11 mm	tan	no print
9667MP	0.06 mm	83# Polycoated Kraft	0.16 mm	tan	3M 200MP
7952MP	0.06 mm	1) 58# Polycoated Kraft 2) 58# Polycoated Kraft	1) 0.11 mm 2) 0.11 mm	tan	3M 200MP	Double lined, available in both roll and sheet form
7962MP	0.06 mm	1) 58# Polycoated Kraft 2) 58# Polycoated Kraft	1) 0.16 mm 2) 0.11 mm	tan	3M 200MP	Double lined, available in both roll and sheet form
468MP	0.13 mm	58# Polycoated Kraft	0.11 mm	tan	3M 468MP 200MP Adhesive
468MPF		Polyester (PET)	0.05 mm	clear	no print
468MC		58# Polycoated Kraft Micro Chanel Liner	0.11 mm	tan	no print
9668MP	0.13 mm	83# Polycoated Kraft	0.16 mm	tan	3M 200MP
7955MP	0.13 mm	1) 58# Polycoated Kraft 2) 58# Polycoated Kraft	1) 0.11 mm 2) 0.11 mm	tan	3M 200MP	Double lined, available in both roll and sheet form
7965MP	0.13 mm	1) 83# Polycoated Kraft 2) 58# Polycoated Kraft	1) 0.16 mm 2) 0.11 mm	tan	3M 200MP	Double lined, available in both roll and sheet form

Transfer Adhesive 467mp

Product Description

Construction

Performance characteristics

Processing

Storage

Durability

Further information